Torsion Testing Experiment

In this torsion testing experiment, the torsion test was evaluated as a system for calculating the torsional rigidity (GJ), modulus of rigidity (G), and the shear yield stress (τ) for aluminum, mild steel, and brass. Both ends of the cylindrical specimen are tightened to hexagonal sockets, which one is fixed to a torque shaft and another is fixed to an input shaft.
By turning the input handwheel, the twisting moment has applied to produce the torque until the specimen fails. At the end of the experiment, it shows that the comparison of the behavior of ductile and brittle materials under torsion.
1. 0 IntroductionThe responses of metals were deal with by mechanical testing to applied forces. This testing includes torsion, tension, hardness, fatigue, creep and stress rupture, and impact tests. Torsion occurs when any shaft is subjected to a torque. The torque causes the shaft to twist. This makes one of the ends to rotate relative to the other; shear stress is induced on any cross-section.
Besides that, torsion testing is made on materials to determine the modulus of elasticity in shear, torsion yield strength, and the modulus of ruptures. The shearing stress at any point on a transverse cross-section varies directly proportional to the distance from the center of the shaft when a simple circular solid shaft is twisted. Therefore, during twisting, the cross-section is initially planar remains a plane and rotates only about the axis of the shaft.
2. 0 Experiment Design
Figure 7: 360-degree protractor scale Figure 6: Three specimen mild steel (top), brass (middle), and aluminium (bottom) after the experiment.
Figure 5: Three specimen mild steel (top), brass (middle), and aluminium (bottom) before the experiment.
Figure 2: Torque meter
Figure 3: Deflection arm, dial gauge, leveling handwheel, and linear potential meter
Figure 4: Input handwheel with a 6-degree protractor scale
Figure 1: Torsion testing machine
2. 1 Apparatus
There were only a few apparatus and materials involved in this experiment, such as:3 pieces of specimens (Aluminium, brass and mild steel)
Vernier Caliper
Torsion Testing Equipment2. 2 Methods
Firstly the apparatus was set up as shown in Figure 1.
The torque meter was switched on to allow the reading to appear on the screen which connected to the torsion testing machine. Three specimens were carried out, mild steel, brass, and aluminium. Each specimen was placed at the hexagonal sockets and it was tightened with the deflection arm. The handwheel was turned 90 degrees each time to take the reading for the angle of twist from the 360 protractor scale and torque from the torque meter of each specimen. Therefore, 12 readings were taken and evenly distributed. After taking the 12 readings, the handwheel was continuously turned until the specimen was fractured.
By the time the specimen was fractured, this shows that the maximum torque and the maximum angle of twist of the specimen. All the readings were recorded in a table form and calculations were done using the equations shown at section Results and Discussion.
2. 3 ProcedureThe specimen as shown in figure 2 below was used for testing. The mild steel specimen was mounted on the torsion testing machine at position no. 4.
It was made sure that on the specimen there was no preload. Before starting the experiment, the handwheel at the input of the worm gear was turned when necessary until the readout of the amplifier is zero. There was still zero error on the amplifier.
Both the indicators at the input and output shaft of the worm gear was set to zero.
The dial gauge of the compensation unit was set to zero.
The revolution counter was reset.
The handwheel was turned through 90° and the Scale Reading at Worm gear input was recorded in revolution(degrees) and the torque value was recorded in digital torque meter(6).3. 0 Results and Discussion
T/J = τ/R = Gφ/L Torsion equation TJ= GφL G=TLJφ τ=πd^432 Where T = Torque applied, Nm G = shear modulus, N/mm2 J = Polar moment of inertia, mm2 φ = Angle of twist, radian L = Gauge Length, mm τ = shear stress, N/mm2 r = radius of the cylindrical bar, mm J=πd432=π(5)432=61.36mm2
1) For mild steel, for example using point (7.25, 17) G=TLJφ=7.25(115)61.36 0.2974=45.80N/mm2 τ=TRJ=7.25(2.5)61.36=0.295N/mm2
For brass, for example using point (5.85, 17) G=TLJφ=5.85(115)61.36(0.297)=36.95N/mm2 τ=TRJ=5.85(2.5)61.36=0.238N/mm2
2) Torsional rigidity is ratio of torque applied about the centroidal axis of a bar at one end of the bar to the resulting torsional angle, when other end is held fixed means torsional rigidity =torqueangle For mild steel, Torsional rigidity = 7. 2517=0. 26 For brass, Torsional rigidity = 5. 8517=0. 344 Therefore, torsional rigidity of mild steel is higher than brass.
3)Specimen: Mild Steel Scale Reading at Worm gear input in Revolution (degrees)
Angle of Twist of Specimen (col. 1/62)
Torque (N. m)90
0
0. 05180
0
0. 05270
2
0. 05360
4
0. 05450
5
0. 10540
8
0. 10630
9
0. 10720
10
0. 35810
11
1. 25900
12
2. 85990
14
5. 001080
17
7. 25Until fracture
4092
21. 05Specimen: Brass Scale Reading at Worm gear input in Revolution (degrees)
Angle of Twist of Specimen (col. 1/62)
Torque (N. m)90
1
0. 05180
4
0. 5270
5
0. 15360
6
0. 55450
7
1. 00540
8
1. 80630
9
2. 80720
11
3. 95810
14
4. 95900
15
5. 55990
16
5. 801080
17
5. 85Until fracture
1047
14. 50Specimen: Aluminium Scale Reading at Worm gear input in Revolution (degrees)
Angle of Twist of Specimen (col. 1/62)
Torque (N. m)90
1
0. 05180
2
0. 15270
4
0. 20360
6
0. 30450
8
0. 45540
9
0. 85630
10
1. 40720
11
2. 30810
13
3. 20900
15
4. 20990
17
5. 251080
18
6. 35Until fracture
311
13. 50Graph of torque against the angle of twist of the specimen (mild steel, brass, and aluminium)
4) Ductility is the ability to deform under tensile stress when subject to stress; brittle materials absorb relatively little energy power to fracture. For ductile material, it will produce a fracture surface along the plane of the maximum shear stress. For brittle material, the fracture plane is normal to the directions of tensile stress. Mild steel is the most ductile compared to brass and aluminium. Therefore, torque is the highest in mild steel. Aluminium is the most brittle compared to mild steel and brass. Therefore, torque is the lowest in aluminium.
5) Cast iron fractures more easily than mild steel.
Mild steel needs more revolution at the worm gear input to fracture the specimen. This is because cast iron is more brittle than mild steel, it is loss ductile. Cast iron has high carbon content causing it to be very brittle and is weak in tension.
4. 0 Error Analysis
From the results we obtained, there was a certain error that happened. Firstly, the input handwheel with 6-degree protractor scale, and the 360-degree protractor scale was not pointing at the zero reading. Thus, this causes zero error in the reading. Secondly, the deflection arm and leveling handwheel was tightened up with the specimen in between the shaft.
However, the specimen was not really tight, which the specimen was not really sustained in the place, whereas it still turned while the handwheel was turning and the torque of the specimen was not accurate. Therefore, the readings obtained might deviate from the correct one.
5. 0 Conclusion and Recommendation
To conclude, ductile materials have higher torsional rigidity, modulus of rigidity, and shear yield stress and it fractures at a higher value of angle of twist, whereas brittle materials have lower torsional rigidity, modulus of rigidity and shear yield stress and it fractures at a lower value of angle of twist.
In this experiment, it shows that mild steel is the most ductile material while aluminum is the most brittle material compared to mild steel and brass. To improve the results, it is important to keep the diameter constant and vary the length of the material to find the mean value so it is more accurate and the zero error is eliminated to find the actual value. The torsion testing machine should be changed, as it is old and less accurate.
6. 0 References:“Laboratory Handbook”, Taylor’s University, 2012/2013.
J. L. Meriam and L. G. Kraige, 2006, Engineering Mechanics Statics. 6th Ed.
http://www. scribd. com/doc/136565/Mechanics-of-Materials-Torsion-Test
http://www. ce. siue. edu/330L/Lab%20Help%20Desk/Metal%20Torsion%20Test/Metal%20Torsion. pdf
http://www. scribd. com/doc/50848950/4/TORSION-TEST-ON-MILD-STEEL-ROD
http://eng. sut. ac. th/metal/images/stories/pdf/Lab_4Torsion_Eng. pdf
http://encyclopedia2. thefreedictionary. com/torsional+rigidity
Approximate price: $22
We value our customers and so we ensure that what we do is 100% original..

With us you are guaranteed of quality work done by our qualified experts.Your information and everything that you do with us is kept completely confidential.You have to be 100% sure of the quality of your product to give a money-back guarantee. This describes us perfectly. Make sure that this guarantee is totally transparent.The Product ordered is guaranteed to be original. Orders are checked by the most advanced anti-plagiarism software in the market to assure that the Product is 100% original. The Company has a zero tolerance policy for plagiarism.The Free Revision policy is a courtesy service that the Company provides to help ensure Customer’s total satisfaction with the completed Order. To receive free revision the Company requires that the Customer provide the request within fourteen (14) days from the first completion date and within a period of thirty (30) days for dissertations.The Company is committed to protect the privacy of the Customer and it will never resell or share any of Customer’s personal information, including credit card data, with any third party. All the online transactions are processed through the secure and reliable online payment systems.By placing an order with us, you agree to the service we provide. We will endear to do all that it takes to deliver a comprehensive paper as per your requirements. We also count on your cooperation to ensure that we deliver on this mandate.